Special Hastelloy C-276 Nickel Alloy Wire Cold Drawing DIN ASTM Standars

Certification
China Shanghai Haosteel Co., Limited certification
China Shanghai Haosteel Co., Limited certification
Good quality, fast delivery, Haosteel has been supplying heat exchanger tubes for many years , we really appreciate your support!

—— Massimiliano Rossi

Haosteel is really a professional supplier, they always give us technical advice and provide good quality tubes with very competitive price!

—— Thomas Hoover

I'm Online Chat Now

Special Hastelloy C-276 Nickel Alloy Wire Cold Drawing DIN ASTM Standars

Special Hastelloy C-276 Nickel Alloy Wire Cold Drawing DIN ASTM Standars
Special Hastelloy C-276 Nickel Alloy Wire Cold Drawing DIN ASTM Standars Special Hastelloy C-276 Nickel Alloy Wire Cold Drawing DIN ASTM Standars Special Hastelloy C-276 Nickel Alloy Wire Cold Drawing DIN ASTM Standars Special Hastelloy C-276 Nickel Alloy Wire Cold Drawing DIN ASTM Standars

Large Image :  Special Hastelloy C-276 Nickel Alloy Wire Cold Drawing DIN ASTM Standars

Product Details:
Place of Origin: China
Brand Name: HAOSTEEL
Certification: SGS, BV, CCIC
Model Number: C-276 alloy
Payment & Shipping Terms:
Minimum Order Quantity: 0.5ton
Packaging Details: In bundles with waterproof material
Detailed Product Description
Material: Hastelloy C-276 / N10276 Type: Nickel Wire Rod
Grade: Nickel Base Alloy Shape: Sheet/strip/pipe/wrie/bar/ect
Standard: ISO 9001 Resistance (μΩ.m): UNS,DIN,ASTM Standars
Technique: Cold Drawing Brand Name: Haosteel
Packages: In Bundles With Waterproof Material Shipping Port: Shanghai
High Light:

nickel steel alloy

,

corrosion resistant steel alloys

ASTM Special Hastelloy C-276 Nickel Alloy Wire Price for Sale

 

Hastelloy-c 276 alloy is a tungsten-chrome-molybdenum alloy with extremely low silicon carbon content, which is considered as a universal anti-corrosion alloy.
It is mainly resistant to wet chlorine, various oxidizing chlorides, chloride solution, sulfuric acid and oxidizing salt, and has good corrosion resistance in low temperature and medium temperature hydrochloric acid.
Therefore, in the past 30 years, in the harsh corrosive environment, such as chemical, petrochemical, flue gas desulphurization, pulp and paper, environmental protection and other industrial fields have been widely used.

Characteristics:

In the two atmosphere states of oxidation and reduction, it has excellent corrosion resistance to most corrosion media.Excellent resistance to pitting corrosion, crevice corrosion and stress corrosion.Higher Mo and Cr contents make the alloy resistant to chloride ion corrosion, and W element further improves the corrosion resistance.At the same time, harrington C-276 alloy is one of the few materials that can resist the corrosion of wet chlorine, hypochlorite and chlorine dioxide solution.
It is one of the few materials that can be applied to hot concentrated sulfuric acid solution.

Standard:

Hastelloy c-276 similar grade:

NiMo16Cr15W (Germany) NC17D (France)

Product ASTM
Alloy Bar Rod Wire B408 , B581
Alloy Thick Plate, Thin Sheet, Coil Strip A240 , A 480 , B409 , B582 , B906
Alloy Seamless Tube and Pipe Fittings B407, B622 , B829
Alloy Welded Normal Bore Pipe ANSI B514 , B619 , B775
Alloy Welded Pipe B515 , B626 , B751
Alloy Welded Pipe Fittings B366
Alloy Forged or rolled pipe flange and forged B462 , B 564
Alloy Forged or rolled billet B472

Chemical Composition

Hastelloy C-276 Chemical composition

Alloy % Ni Cr Mo Fe W Co C Mn Si V P S
C276 Min. 62.5-67.5 14.5 15 4 3              
Max. 16.5 17 7 4.5 2.5 0.01 1 0.08 0.35 0.04 0.03

Executive standards: UNS N10276, ASTM B575, ASME SB575, DIN/EN 2.4819

Tensile strength: v/d b is greater than or equal to 730Mpa, elongation: irradiation is greater than or equal to 40%, hardness: HRB is less than or equal to 100.Hartz C - 276 alloy hot forming is instantly annealing at 1150 ℃, and water quenching.The strength of harrington C-276 alloy can be increased by cold deformation.

Haversian C-276 alloy and ordinary austenite stainless steel have similar forming performance.However, as it is stronger than normal austenite stainless steel, it will have greater stress during cold forming.In addition, this material is machined and hardened much faster than ordinary stainless steel, so it is necessary to adopt half-way annealing during extensive cold forming processing.

Welding and heat treatment

The welding performance of c-276 alloy is similar to that of ordinary austenite stainless steel.This material can be used in most welds.Before using a welding method for c-276 welding, measures must be taken to minimize the corrosion resistance of the weld and the heat affected zone, such as GTAW, GMAW, submerged arc welding or some other welding method that can minimize the corrosion resistance of the weld and the heat affected zone.

Hartz C - 276 alloy solid solution heat treatment includes two processes: a. in 1040℃ ~ 1150℃ heating;

B. rapid cooling to black state in two minutes (about 400 ℃), the processed material has good corrosion resistance.Therefore, it is not effective to conduct stress relief heat treatment only on harrington C-276 alloy.Clean up any dirt that may cause carbon in the heat treatment process, such as oil on the alloy's surface, before heat treatment.

Form Specification Supply Form Others
Sheet Thickness:0.40-4.75mm,General Width:1000,1219,1500mm Whole Coil or piece of it Cold Annealed,Surface 2B,2E
Plate

Thickness:4.76-60mm,Width:1500,2000,2500mm,Length:3000,6000,

8000,8500mm(Under 10mm plate can be coiled)

Whole Coil or piece of it Single hot rolling,Solid solution annealed state,Surface 1D
Belt Thickness:0.10-3.0mm,Width:50-500mm Whole Coil or Specified size Cold Annealed,Surface 2B,2E
Bar & Rod Rolled barΦ5-45mm,Length≤1500mm Polished Bar(circle,Square) Solution annealing,descaling
Forged barΦ26-245mm,Length≤4000mm
Weld tube Outer diameterΦ4.76-135mm,Wall Thickness0.25-4.00mm,Length:≤35000 mm Base on your requirement Use for PHE
Seamless Tube Outer diameterΦ3-114mm,Wall Thickness0.2-4.5mm Base on your requirement Use for PHE
Wire Outer diameterΦ0.1-13mm Base on your requirement Ni & Ni alloy, Ti & Ti alloy
Forged piece roundness and square alloy Base on your requirement Steel, Alloy
Flangs All kinds of Flangs Base on your requirement Steel, Alloy
Welding Material Coil wire Φ0.90mm/1.2mm/1.6mm Base on your requirement Certificate of Origin:America, Sweden, Britain, Germany, Austria, Italy, France.
Straight WireΦ1.2mm/1.6mm/2.4mm/3.2mm/4.0mm
Welding rodΦ2.4mm/3.2mm/4.0mm
Tube Elbow, three links, four links, different diameter size Base on your requirement Ni & Ni alloy, Ti & Ti alloy
Explosive bonded laminate Raw Sheet Thickness≥2mm Base on your requirement Ni & Ni alloy, Ti & Ti alloy

 