436L Standard Stainless Steel Sheet Thickness 0.3~3 MM Cold Rolled 2B Finish
Description:
436 stainless steel is a modified steel grade of 434 that reduces the tendency to "wrinkle" during relatively stringent stretch forming operations. 430 is used as a molded product for automotive interior trim panels, and uses 434 and 436 stainless steel when better corrosion resistance is required.
436 stainless steel:
Name: Ferritic stainless steel
Standard: AISI, ASTM
Model Number: 436
UNS number: S43600
Chemical composition:
Carbon C: ≤ 0.12
Manganese Mn: ≤1.00
Silicon Si: ≤1.00
Chromium Cr: 16.0~18.0
Nickel Ni2:-
Phosphorus P: ≤0.04
Sulfur S: ≤0.03
Molybdenum Mo: 0.75~1.25
Nb: (5C~0.80)
Mechanical Properties at Room Temperature
Properties: Annealed
Ultimate Tensile Strength: 77 KSI min (531 MPa min)
Yield Strength: (0.2% Offset) 53 KSI min (365 MPa min)
Elongation: 22% min
Hardness: HRB 89 max
Finishes
#2B–Smooth finish produced by cold rolling, annealing and descaling. A light cold rolling pass is added after anneal with polished rolls giving it a brighter finish than 2D.
#BA-Bright annealed cold rolled and bright annealed
#CBA-Course bright annealed cold rolled matte finish and bright anneal
#2-Cold Rolled
#2BA–Smooth finish produced by cold rolling and bright annealing. A light pass using highly polished rolls produces a glossy finish. A 2BA finish may be used for lightly formed applications where a glossy finish is desired in the formed part.
Polished-Various grit finish for specific polish finished requirements
*Not all finishes are available for all alloys – Contact Haosteel Sales for more information