Product Details:
Payment & Shipping Terms:
|
| Product: | AISI 301 1.4310 Stainless Steel Strip With Excellent Quality | Grade: | 301 201 304 304L 410 420 430 321 316 316L Etc |
|---|---|---|---|
| Surface: | Mirror Finish, Hair Line, BA 2B Finish | Technique: | Hot Rolled Cold Rolled |
| Standard: | AISI, ASTM A167 A666 | Length: | Customer's Requirement |
| Thickness: | 0.2mm ~ 6mm | Width: | 5mm ~ 600mm |
| High Light: | stainless steel sheet roll,thin steel strips |
||
AISI 301 1.4310 Stainless Steel Strip 2B BA soft annealed 1/2H 3/4H H hardness
Specification:
| Product Name | 301 Stainless steel coil/strip |
| Process | Hot Rolled/Cold Rolled |
| Grade | 200/300/400 series(301 310s 309s 304 316 316l 201 202 321 410 430......) |
| Surface | No.1/ 2B/ BA/No.4/ HL |
| Standard | AISI ASTM JIS EN DIN ...... |
| Thickness | 0.2-3mm(cold rolled) 3-6mm(hot rolled) |
| Width | 5mm ~ 600mm |
Chemical Composition:
|
Element |
Percent by Weight Maximum Unless Range is Specified |
| Carbon | 0.15 maximum |
| Manganese | 2.00 maximum |
| Phosphorus | 0.045 maximum |
| Sulfur | 0.030 maximum |
| Silicon | 0.75 maximum |
| Chromium | 16.00-18.00 |
| Nickel | 6.00-8.00 |
| Nitrogen | 0.10 maximum |
Mechanical properties:
| Condition |
Tensile Strength, Min. Ksi(MPa) |
0.2% Yield Strength, Min. Ksi (MPa) |
Elong. In 2" (50mm) %, Min. |
||
| Annealed | 75 | 515 | 30 | 205 | 40 |
| 1/4 Hard | 125 | 862 | 75 | 517 | 25 |
| 1/2 Hard | 150 | 1,034 | 110 | 758 | 18 |
| 3/4 Hard | 175 | 1,207 | 125 | 931 | 12 |
| Full Hard | 185 | 1,276 | 140 | 965 | 9 |
Tempered:
|
Temper |
Condition |
Tension | ||||||||||
| Longitudinal | Transverse | |||||||||||
|
0.2% Y.S. Ksi (MPa) |
Modulus 10 6psi (GPa) |
0.2% Y.S. Ksi (MPa) |
Modulus 10 6psi (GPa) |
|||||||||
|
Annealed 1/4 Hard |
As annealed As rolled Stress relieved |
36 80 77 |
(248) (552) (531) |
31.0 28.0 28.7 |
(214) (193) (198) |
36 84 79 |
(248) (579) (545) |
30.6 28.6 27.0 |
(211) (197) (186) |
|||
| 1/2 Hard | As rolled Stress relieved |
122 128 |
(841) (883) |
26.8 27.9 |
(185) (192) |
123 130 |
(848) (896) |
28.1 28.6 |
(194) (197) |
|||
| 3/4 Hard | As rolled Stress relieved |
142 155 |
(979) (1,069) |
25.8 27.3 |
(178) (188) |
145 155 |
(1,000) (1,069) |
27.5 28.8 |
(190) (199) |
|||
| Full Hard | As rolled Stress relieved |
160 175 |
(1,103) (1,207) |
25.2 28.4 |
(174) (196) |
163 181 |
(1,124) (1,248) |
28.4 30.5 |
(196) (210) |
|||
| Compression | ||||||||||||
|
Annealed 1/4 Hard |
As annealed As rolled Stress relieved |
38 50 73 |
(262) (345) (503) |
30.6 28.2 28.8 |
(211) (194) (199) |
38 91 84 |
(262) (627) (579) |
30.3 28.2 30.6 |
(209) (194) (211) |
|||
| 1/2 Hard | As rolled Stress relieved |
90 111 |
(621) (765) |
27.5 29.2 |
(190) (201) |
142 144 |
(979) (993) |
27.5 29.8 |
(190) (205) |
|||
| 3/4 Hard | As rolled Stress relieved |
100 133 |
(690) (917) |
26.5 27.5 |
(183) (190) |
170 176 |
(1,172) (1,213) |
27.9 29.5 |
(192) (203) |
|||
| Full Hard | As rolled Stress relieved |
115 169 |
(793) (1,165) |
24.6 27.7 |
(170) (191) |
191 209 |
(1,317) (1,441) |
29.4 29.6 |
(203) (204) |
|||